Product Description
Description:
ABS Resin PA-757 A01 Resin Exhibits High Rigidity, Medium Impact Strength And Pre Color For Products.
Application:
Household Appliances/Boxes For Cosmetics/Office Appliances.
Product Details
|
Properties
|
ISO Test Method
|
Test Condition
|
Unit
|
PA-757 A01
|
|
Melt Flow Index
|
1133
|
220oC×10KG
|
ml/10 min
|
18
|
|
Mass Density
|
1183
|
23 oC
|
g/cm3
|
1.07
|
|
Tensile Strength
|
527
|
50 mm/min, yield
|
MPa
|
47
|
|
|
|
50 mm/min, break
|
MPa
|
35
|
|
Tensile Elongation
|
527
|
50 mm/min
|
%
|
30
|
|
Flexural Strength
|
178
|
2 mm/min
|
MPa
|
70
|
|
Flexural Modulus
|
|
2 mm/min
|
GPa
|
2.4
|
|
Izod Impact Strength
|
180/1A
|
23 oC Notched
|
KJ/m2
|
17
|
|
|
|
-30 oC Notched
|
KJ/m2
|
-
|
|
Charpy Impact
Strength
|
179
|
23 oC Notched
|
KJ/m2
|
17
|
|
|
|
-30 oC Notched
|
KJ/m2
|
-
|
|
Vicat Softening Temp.
|
306
|
1 Kg,50 oC/hr
|
oC
|
106
|
|
|
|
5 Kg,50 oC/hr
|
oC
|
102
|
|
Heat Distortion Temp.
|
75/A
|
1.8 MPa Unannealed
|
oC
|
-
|
|
|
|
1.8 MPa Annealed
|
oC
|
98
|
|
Coefficient of Linear
Thermal Expansion
|
11359
|
-
|
-
|
7.9 x 10-6
|
|
Flammability
|
-
|
UL-94
|
-
|
1.6mm HB
|
|
Mold Shrinkage
|
294-4
|
-
|
%
|
0.4~0.7
|
|
Symbol
|
1043
|
-
|
-
|
>ABS<
|
|
Symbol
|
1043
|
-
|
-
|
>ABS<
|
|
| |