1. LLDPE film grade
|
Tests
|
Value
|
Unit
|
|
Melt Flow Rate (MFR)
|
2.0±0.4
|
g/10min
|
|
Density
|
920±2
|
Kg/cm3
|
|
Tensile Strength at Yield
|
8
|
Mpa ≥
|
|
Tensile Strength at Break
|
12
|
Mpa ≥
|
|
haze
|
15
|
%≤
|
|
Packing
|
In 25 kg PP woven bags,20MT/20'FCL
|
2. LLDPE for Master Batch Use
|
Tests
|
Value
|
Unit
|
|
Melt Flow Rate (MFR)
|
20
|
g/10min
|
|
Density
|
0.924
|
g/cm3
|
|
Tensile Strength
|
MD12
|
Mpa
|
|
TD 10
|
|
Elongation at Yield
|
13
|
%
|
|
Elongation at Break
|
200
|
|
Dark Drop Impact
|
105
|
g
|
|
Brittle Temperature(F 50)
|
-70
|
°C
|
|
Vicat Softening Point
|
90
|
°C
|
|
Packing
|
In 25 kg woven bags,20MT/20'FCL
|
3. LLDPE Powder Rotational Molding Grade for Tank Use
|
Tests
|
Value
|
Unit
|
|
Melt Flow Rate (MFR)
|
3.2
|
g/10min
|
|
Density
|
0.939
|
g/cm3
|
|
Melting Point
|
127
|
°C
|
|
Tensile Yield Strength
|
21
|
Mpa
|
|
Tensile Strength at Break
|
28
|
Mpa
|
|
Elongation at Break
|
1,100
|
%
|
|
Flexural Modulus
|
750
|
Mpa
|
|
Brittle Temperature
|
<-60
|
°C
|